What if NM500 wear-resistant steel plate breaks during bending

Once NM500 wear-resistant steel plate breaks, it can no longer be used. Its pressure bearing capacity has been weakened, and how can it be put into production. All we have to do is find the reason, prevent it and avoid such things from happening again. Why does such a hard steel plate break? In fact, the harder the steel plate is, the more likely it is to break during bending. It is necessary to select an appropriate method for processing.

During the bending process of NM500 wear-resistant steel plate, the acceptable radius range and the opening size of the lower die are selected, so that the fracture can be prevented during processing. NM500 wear-resistant steel plate is mainly used to produce various machinery and parts. The broken steel plate will affect the quality of finished products. The broken part shall be cut off and the remaining untreated part shall be used. In that way, the size of the NM500 steel plate will be reduced and its use will be limited.

In fact, there are many ways to avoid the fracture of NM500 wear-resistant steel plate, especially in the process of bending or cutting, moderate heating can soften the steel plate, reduce the hardness first and then temper, so that its performance will be restored. However, the temperature difference in the processing process should be well controlled, otherwise NM500 wear-resistant steel plate may be lost.