A633Gr.D and A633Gr.E are American standard normalized high-strength low-alloy steel plates for welding, riveting, and bolting structures.
Chemical composition of A633Gr.D steel plate:
Grade | C | Si | Mn | P | S | Ni | Cr | Mo | Cu |
A633 Gr.D | ≤0.2 | 0.15-0.5 | 1-1.6 | ≤0.03 | ≤0.03 | ≤0.25 | ≤0.25 | ≤0.08 | ≤0.35 |
A633 Gr.D steel plate mechanical properties:
Delivery Status | Thickness | Mechanical properties | ||
Normalizing | >40-65mm | Re(MPa) | ≥345 | |
Rm(MPa) | 485-620 | |||
A200(%) | ≥18 | A50≥23% | ||
>65-100mm | Re(MPa) | ≥315 | ||
Rm(MPa) | 450-590 | |||
A200(%) | ≥18 | A50≥23% |
Melting analysis of chemical composition of A633 Gr.E steel plate:
Grade | C | Si | Mn | P | S | Nb | V | Alt | N |
A633 Gr.E | ≤0.22 | 0.15-0.5 | 1.15-1.5 | ≤0.03 | ≤0.03 | 0.010-0.05 | 0.04-0.11 | ≥0.018 | ≤0.03 |
Composition remarks: Alt≥0.018 or vanadium-nitrogen ratio>4:1.
Mechanical properties of A633 Gr.E steel plate:
Delivery Status | Thickness | Mechanical properties | ||
Normalizing | ≤100mm | Re(MPa) | ≥415 | |
Rm(MPa) | 550-690 | |||
A200(%) | ≥18 | A50≥23% | ||
>100-150mm | Re(MPa) | ≥380 | ||
Rm(MPa) | 515-655 | |||
A200(%) | ≥18 | A50≥23% |
A633Gr.D and A633Gr.E steel plate technical standard and scope of application:
A633Gr.D and A633Gr.E steel implement ASTM A633/A633M standard. They are mainly used in bridges, ships, vehicles, boilers, high-pressure vessels, oil and gas pipelines, large steel structures and other manufacturing fields.